The importance of concrete in modern society cannot be under-estimated. Look around you and you will find concrete structures everywhere such as buildings, roads, bridges, and dams. There is no escaping the impact concrete makes on your everyday life. So what is it?

Concrete is a composite material which is made up of a filler and a binder. The binder (cement paste) "glues" the filler together to form a synthetic conglomerate. The constituents used for the binder are cement and water, while the filler can be fine or coarse aggregate. The role of these constituents will be discussed in this section.

Cement, as it is commonly known, is a mixture of compounds made by burning limestone and clay together at very high temperatures ranging from 1400 to 1600 [[ring]]C.

Although there are other cements for special purposes, this module will focus solely on portland cement and its properties. The production of portland cement begins with the quarrying of limestone, CaCO3. Huge crushers break the blasted limestone into small pieces. The crushed limestone is then mixed with clay (or shale), sand, and iron ore and ground together to form a homogeneous powder. However, this powder is microscopically heterogeneous. (See flowchart.)


Figure 1: A flow diagram of Portland Cement production.
The mixture is heated in kilns that are long rotating steel cylinders on an incline. The kilns may be up to 6 meters in diameter and 180 meters in length. The mixture of raw materials enters at the high end of the cylinder and slowly moves along the length of the kiln due to the constant rotation and inclination. At the low end of the kiln, a fuel is injected and burned, thus providing the heat necessary to make the materials react. It can take up to 2 hours for the mixture to pass through the kiln, depending upon the length of the cylinder.


Rotary kiln;
As the mixture moves down the cylinder, it progresses through four stages of transformation. Initially, any free water in the powder is lost by evaporation. Next, decomposition occurs from the loss of bound water and carbon dioxide. This is called calcination. The third stage is called clinkering. During this stage, the calcium silicates are formed. The final stage is the cooling stage.

The marble-sized pieces produced by the kiln are referred to as clinker. Clinker is actually a mixture of four compounds which will be discussed later. The clinker is cooled, ground, and mixed with a small amount of gypsum (which regulates setting) to produce the general-purpose portland cement.

Water is the key ingredient, which when mixed with cement, forms a paste that binds the aggregate together. The water causes the hardening of concrete through a process called hydration. Hydration is a chemical reaction in which the major compounds in cement form chemical bonds with water molecules and become hydrates or hydration products. Details of the hydration process are explored in the next section. The water needs to be pure in order to prevent side reactions from occurring which may weaken the concrete or otherwise interfere with the hydration process. The role of water is important because the water to cement ratio is the most critical factor in the production of "perfect" concrete. Too much water reduces concrete strength, while too little will make the concrete unworkable. Concrete needs to be workable so that it may be consolidated and shaped into different forms (i.e.. walls, domes, etc.). Because concrete must be both strong and workable, a careful balance of the cement to water ratio is required when making concrete.

Aggregates are chemically inert, solid bodies held together by the cement. Aggregates come in various shapes, sizes, and materials ranging from fine particles of sand to large, coarse rocks. Because cement is the most expensive ingredient in making concrete, it is desirable to minimize the amount of cement used. 70 to 80% of the volume of concrete is aggregate keeping the cost of the concrete low. The selection of an aggregate is determined, in part, by the desired characteristics of the concrete. For example, the density of concrete is determined by the density of the aggregate. Soft, porous aggregates can result in weak concrete with low wear resistance, while using hard aggregates can make strong concrete with a high resistance to abrasion.

Aggregates should be clean, hard, and strong. The aggregate is usually washed to remove any dust, silt, clay, organic matter, or other impurities that would interfere with the bonding reaction with the cement paste. It is then separated into various sizes by passing the material through a series of screens with different size openings.


Table 1: Classes of Aggregates class examples of aggregates used uses
ultra-lightweight vermiculite
ceramic spheres
perlite lightweight concrete which can be sawed or nailed, also for its insulating properties
lightweight expanded clay
shale or slate
crushed brick used primarily for making lightweight concrete for structures, also used for its insulating properties.
normal weight crushed limestone
sand
river gravel
crushed recycled concrete used for normal concrete projects
heavyweight steel or iron shot
steel or iron pellets used for making high density concrete for shielding against nuclear radiation


The choice of aggregate is determined by the proposed use of the concrete. Normally sand, gravel, and crushed stone are used as aggregates to make concrete. The aggregate should be well-graded to improve packing efficiency and minimize the amount of cement paste needed. Also, this makes the concrete more workable.


Properties of Concrete

Concrete has many properties that make it a popular construction material. The correct proportion of ingredients, placement, and curing are needed in order for these properties to be optimal.

Good-quality concrete has many advantages that add to its popularity. First, it is economical when ingredients are readily available. Concrete's long life and relatively low maintenance requirements increase its economic benefits. Concrete is not as likely to rot, corrode, or decay as other building materials. Concrete has the ability to be molded or cast into almost any desired shape. Building of the molds and casting can occur on the work-site which reduces costs.

Concrete is a non-combustible material which makes it fire-safe and able withstand high temperatures. It is resistant to wind, water, rodents, and insects. Hence, concrete is often used for storm shelters.

Concrete does have some limitations despite its numerous advantages. Concrete has a relatively low tensile strength (compared to other building materials), low ductility, low strength-to-weight ratio, and is susceptible to cracking. Concrete remains the material of choice for many applications regardless of these limitations.

Hydration of Portland Cement

Concrete is prepared by mixing cement, water, and aggregate together to make a workable paste. It is molded or placed as desired, consolidated, and then left to harden. Concrete does not need to dry out in order to harden as commonly thought.

The concrete (or specifically, the cement in it) needs moisture to hydrate and cure (harden). When concrete dries, it actually stops getting stronger. Concrete with too little water may be dry but is not fully reacted. The properties of such a concrete would be less than that of a wet concrete. The reaction of water with the cement in concrete is extremely important to its properties and reactions may continue for many years. This very important reaction will be discussed in detail in this section.

Portland cement consists of five major compounds and a few minor compounds. The composition of a typical portland cement is listed by weight percentage in Table 2.

Cement Compound Weight Percentage Chemical Formula
Tricalcium silicate 50 % Ca3SiO5 or 3CaO.SiO2
Dicalcium silicate 25 % Ca2SiO4 or 2CaO.SiO2
Tricalcium aluminate 10 % Ca3Al2O6 or 3CaO .Al2O3
Tetracalcium aluminoferrite 10 % Ca4Al2Fe10 or 4CaO.Al2O3.Fe2O3
Gypsum 5 % CaSO4.2H2O

Composition of portland cement with chemical composition and weight percent.
When water is added to cement, each of the compounds undergoes hydration and contributes to the final concrete product. Only the calcium silicates contribute to strength. Tricalcium silicate is responsible for most of the early strength (first 7 days). Dicalcium silicate, which reacts more slowly, contributes only to the strength at later times. Tricalcium silicate will be discussed in the greatest detail.

The equation for the hydration of tricalcium silicate is given by:

Tricalcium silicate + Water--->Calcium silicate hydrate+Calcium hydroxide + heat

2 Ca3SiO5 + 7 H2O ---> 3 CaO.2SiO2.4H2O + 3 Ca(OH)2 + 173.6kJ

Upon the addition of water, tricalcium silicate rapidly reacts to release calcium ions, hydroxide ions, and a large amount of heat. The pH quickly rises to over 12 because of the release of alkaline hydroxide (OH-) ions. This initial hydrolysis slows down quickly after it starts resulting in a decrease in heat evolved.

The reaction slowly continues producing calcium and hydroxide ions until the system becomes saturated. Once this occurs, the calcium hydroxide starts to crystallize. Simultaneously, calcium silicate hydrate begins to form. Ions precipitate out of solution accelerating the reaction of tricalcium silicate to calcium and hydroxide ions. (Le Chatlier's principle). The evolution of heat is then dramatically increased.

The formation of the calcium hydroxide and calcium silicate hydrate crystals provide "seeds" upon which more calcium silicate hydrate can form. The calcium silicate hydrate crystals grow thicker making it more difficult for water molecules to reach the unhydrated tricalcium silicate. The speed of the reaction is now controlled by the rate at which water molecules diffuse through the calcium silicate hydrate coating. This coating thickens over time causing the production of calcium silicate hydrate to become slower and slower.



Schematic illustration of the pores in calcium silicate through different stages of hydration.

The above diagrams represent the formation of pores as calcium silicate hydrate is formed. Note in diagram (a) that hydration has not yet occurred and the pores (empty spaces between grains) are filled with water. Diagram (b) represents the beginning of hydration. In diagram (c), the hydration continues. Although empty spaces still exist, they are filled with water and calcium hydroxide. Diagram (d) shows nearly hardened cement paste. Note that the majority of space is filled with calcium silicate hydrate. That which is not filled with the hardened hydrate is primarily calcium hydroxide solution. The hydration will continue as long as water is present and there are still unhydrated compounds in the cement paste.

Dicalcium silicate also affects the strength of concrete through its hydration. Dicalcium silicate reacts with water in a similar manner compared to tricalcium silicate, but much more slowly. The heat released is less than that by the hydration of tricalcium silicate because the dicalcium silicate is much less reactive. The products from the hydration of dicalcium silicate are the same as those for tricalcium silicate:

Dicalcium silicate + Water--->Calcium silicate hydrate + Calcium hydroxide +heat

2 Ca2SiO4 + 5 H2O---> 3 CaO.2SiO2.4H2O + Ca(OH)2 + 58.6 kJ

The other major components of portland cement, tricalcium aluminate and tetracalcium aluminoferrite also react with water. Their hydration chemistry is more complicated as they involve reactions with the gypsum as well. Because these reactions do not contribute significantly to strength, they will be neglected in this discussion. Although we have treated the hydration of each cement compound independently, this is not completely accurate. The rate of hydration of a compound may be affected by varying the concentration of another. In general, the rates of hydration during the first few days ranked from fastest to slowest are:

tricalcium aluminate > tricalcium silicate > tetracalcium aluminoferrite > dicalcium silicate.


Heat is evolved with cement hydration. This is due to the breaking and making of chemical bonds during hydration. The heat generated is shown below as a function of time.



Rate of heat evolution during the hydration of portland cement

The stage I hydrolysis of the cement compounds occurs rapidly with a temperature increase of several degrees. Stage II is known as the dormancy period. The evolution of heat slows dramatically in this stage. The dormancy period can last from one to three hours. During this period, the concrete is in a plastic state which allows the concrete to be transported and placed without any major difficulty. This is particularly important for the construction trade who must transport concrete to the job site. It is at the end of this stage that initial setting begins. In stages III and IV, the concrete starts to harden and the heat evolution increases due primarily to the hydration of tricalcium silicate. Stage V is reached after 36 hours. The slow formation of hydrate products occurs and continues as long as water and unhydrated silicates are present.

STRENGTH of Concrete

The strength of concrete is very much dependent upon the hydration reaction just discussed. Water plays a critical role, particularly the amount used. The strength of concrete increases when less water is used to make concrete. The hydration reaction itself consumes a specific amount of water. Concrete is actually mixed with more water than is needed for the hydration reactions. This extra water is added to give concrete sufficient workability. Flowing concrete is desired to achieve proper filling and composition of the forms. The water not consumed in the hydration reaction will remain in the microstructure pore space. These pores make the concrete weaker due to the lack of strength-forming calcium silicate hydrate bonds. Some pores will remain no matter how well the concrete has been compacted.